C36000 brass is a popular brass type of copper, lead, and zinc. Its composition ranges from 58% to 63% copper, 2.5% to 3.7% lead, and the remaining balance is zinc. The lead content in C36000 brass gives it high machinability; however, it reduces its electrical conductivity and should be kept in mind when selecting the material for specific applications.
| Element | Content (%) |
|---|---|
| Cu | 61.5 |
| Pb | 3 |
| Zn | 35.5 |
C36000 brass has excellent physical properties. It has a density of around 8.49 g/cm3 and a melting point of 890°C. It also has good thermal conductivity, enabling it to quickly transfer heat. These physical properties make it a suitable material for applications where heat is present.
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8.49 g/cm3 | 0.307 lb/in³ |
| Melting point | 885°C | 1630°F |
C36000 brass has good mechanical properties, especially strength and flexibility. Its ultimate tensile strength is about 410 MPa, and its Brinell hardness ranges from 80 to 90 HB. It can be easily machined but requires more power to cut than other brass alloys.
| Properties | Metric | Imperial |
|---|---|---|
| Thermal expansion co-efficient (@ 20-300°C/ 68-572°F) | 20.5 µm/m°C | 11.4 µin/in°F |
| Thermal conductivity (@ 20°C/ 68°F) | 115 W/mK | 798 BTU in/hr.ft².°F |
C36000 brass has a wide range of applications across various industries. It is commonly used to manufacture fasteners, valves, fittings, and connectors. It is also used in plumbing fixtures, gears, and electrical components such as terminals, connectors, and switch parts.
ASTM B16
SAE J461
SAE J463
C36000 brass has a medium-hardness rating, making it suitable for applications where both hard and soft materials are required. Work-hardening can increase its hardness, which involves stretching or forming the material.
C36000 brass can be heat-treated to increase strength and flexibility. However, the process should be carefully controlled to prevent the formation of intermetallic compounds that can weaken the material. The recommended temperature range for annealing is between 370°C to 650°C.
C36000 brass can be welded using various methods, such as gas tungsten arc welding (GTAW), gas metal arc welding (GMAW), and resistance welding. However, it is important to ensure that the welding process does not generate excessive heat, which can cause cracks and weaken the material.
C36000 brass has good resistance to corrosion, especially in seawater and marine environments. Its high zinc content makes it resistant to dezincification, a process where the zinc is selectively leached out of the brass alloy in specific environments.