230 Brass is composed mainly of copper and zinc, which gives it excellent chemical resistance. It won't corrode or rust easily when exposed to moisture or harsh chemicals like acids or bases. This makes it perfect for use in areas where corrosion could be problematic, such as marine environments or near corrosive liquids or gases.
| Chemistry Information | |
| Element | Percentage |
| Cu | 85 |
| Zn | 15 |
Brass 230 Physical Properties
UNS C23000 also has excellent physical properties, making it a great choice for industrial use. It has high tensile strength and hardness, making it strong enough to withstand heavy loads and wear and tear over time without breaking down quickly. 230 Brass malleability also makes it relatively easy to shape into complex components.
| Properties | Metric | Imperial |
|---|---|---|
| Melting point-liquidus | 1027°C | 1880°F |
| Melting point-solidus | 988°C | 1810°F |
| Density (@20°C/68°F) | 8.75 gm/cm3 | 0.316 lb/in3 |
230 Brass Mechanical Properties
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 269-724 MPa | 39-105 ksi |
| Yield strength | 69-434 MPa | 10-70 ksi |
| Elongation | 55% | 55% |
| Poisson's ratio | 0.34 | 0.34 |
| Elastic modulus | 117 GPa | 16969 ksi |
Brass 230 Equivalent
| CDA | ASTM | SAE | AMS | Federal | Military | Other |
| C23000 | B927 B927M |
Brass 230 Specifications
Brass 230 Applications
Brass UNS C23000 has many different applications in the manufacturing industry. It can manufacture components for cars and ships, aerospace parts and medical devices. It's also used to make jewellery and other decorative items. Because of its versatility, it's one of the most popular alloys used in modern manufacturing.
230 Brass Corrosion Resistance
One of the biggest benefits of brass 230 is its impressive corrosion resistance compared to other metals like steel or aluminium. This makes it ideal for use in areas with high humidity or salty air levels and areas prone to frequent exposure to water or other corrosive elements like oil or gasoline fumes.