The following table shows the mechanical properties of UNS C27000 rods as a function of heat treatment and thickness.
| Temper | Thickness | Tensile Str. | Yield Str. | Elong. | Rockwell | Shear Str. | |||
|---|---|---|---|---|---|---|---|---|---|
| B | C | F | 30T | ||||||
| OS050 | 25.4 mm (1 in) | 331 MPa (48 ksi) | 110 MPa (116 ksi) | 65% | - | - | 65 | - | 234 MPa (34 ksi) |
The chemical composition of UNS C27000 yellow brass is outlined in the following table.
| Element | Content (%) |
|---|---|
| Copper, Cu | 63-68.5 |
| Lead, Pb | 0.09 |
| Iron, Fe | 0.07 |
| Zinc, Zn | Remainder |
Equivalent materials to UNS C27000 copper alloy include:
AMS 4710
AMS 4712
AMS 4713
ASTM B134
ASTM B135
ASTM B587
ASTM F467
ASTM F468
QQ W321
SAE J461
SAE J463