C95800 Lead Free Nickel Aluminum Bronze
Henan Gnee New Material Co., Ltd. is one of the most professional manufacturers and suppliers of c95800 lead free nickel aluminum bronze in China, specialized in providing high quality copper products with competitive price. Welcome to buy discount c95800 lead free nickel aluminum bronze for sale here from our factory. Customized orders are welcome.
C95800
Similar or equivalent specification
| CDA | ASTM | SAE | AMS | Federal | Military | Other |
|---|---|---|---|---|---|---|
| C95800 | B505 B505M |
QQ-C-390, G8 | Apha Nickel-Aluminum bronze |
Chemical composition
| Cu% | Pb% | Fe%1 | Ni%1,2 | Al% | Mn% | Si% | |||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Chemical composition according to ASTM B505/B505M-23 1Fe content shall not exceed Ni content. 2Ni value includes Co. Unless otherwise noted, single values represent maximums. |
|||||||||||
| 79.00 min |
0.03 |
3.50- 4.50 |
4.00- 5.00 |
8.50- 9.50 |
0.80- 1.50 |
0.10 |
|||||
Machinability
| Copper alloy UNS No. | Machinability rating | Density (lb/in3 at 68 °F) |
|---|---|---|
| C95800 | 20 | 0.276 |
Mechanical properties
|
Mechanical properties according to ASTM B505/B505M-23 Note: C95800 provided as cast or temper annealed. |
|||||||||||
| Tensile strength, min | Yield strength, at 0.5% extension under load, min | Elongation, in 2 in. or 50 mm min | Brinell hardness (3000 kg load) | Remarks | |||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| ksi | MPa | ksi | MPa | % | typical BHN | ||||||
| 85 | 586 | 35 | 241 | 18 | 159 | ||||||
Physical properties
| US Customary | Metric | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
|
Physical properties provided by CDA *Field strength 16 kA/m |
|||||||||||
| Melting point - liquidus | 1940 °F | 1060 °C | |||||||||
| Melting point - solidus | 1910 °F | 1043 °C | |||||||||
| Density | 0.276 lb/in3 at 68 °F | 7.64 gm/cm3 at 20 °C | |||||||||
| Specific gravity | 7.64 | 7.64 | |||||||||
| Electrical conductivity | 7% IACS at 68 °F | 0.041 MegaSiemens/cm at 20 °C | |||||||||
| Thermal conductivity | 20.8 Btu/sq ft/ft hr/°F at 68 °F | 36 W/m at 20 °C | |||||||||
| Coefficient of thermal expansion 68-572 | 9 · 10-6 per °F (68-572 °F) | 15.5 · 10-6 per °C (20-300 °C) | |||||||||
| Specific heat capacity | 0.105 Btu/lb/°F at 68 °F | 440 J/kg at 20 °C | |||||||||
| Modulus of elasticity in tension | 16500 ksi | 114000 MPa | |||||||||
| Magnetic Permeability* | 1.05 | 1.05 | |||||||||
| Poisson's Ratio | 0.32 | 0.32 | |||||||||
Fabrication properties
|
Fabrication properties provided by CDA |
|||||||||||
| Technique | Suitability | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Soldering | Good | ||||||||||
| Brazing | Fair | ||||||||||
| Oxyacetylene welding | Not recommended | ||||||||||
| Gas shielded arc welding | Good | ||||||||||
| Coated metal arc welding | Good | ||||||||||
| Machinability rating | 20 | ||||||||||
Thermal properties
|
Thermal properties provided by CDA *Temperature is measured in Fahrenheit. **For stress relief, solution treatment and annealing - time is measured in hours/inch of thickness. For precipitation heat treatment - time is measured in hours. |
|||||||||||
| Treatment | Value* | Time** | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Stress relief | 600 | ||||||||||
| Solution treatment | 0 | ||||||||||